QC Lubricants
CAGE CODE 9Y364
7360 Milnor St. Philadelphia, PA 19136
(215) 333-4187
Direct Line

Toll Free
With Extension (800) 887-2436
For Technical Assistance:
Dial Extension 203 for Stan Jakubowski
For Sales:
Dial Extension 211 for Lu Ann Quinn or 224 for Lindsay Romero
Email Lu Ann Quinn  ♦   Email Lindsay Romero


Home

We actively supply a comprehensive line of MIL-SPEC  and commercial lubricants.

 

Back to Tectyl Main Page
Mil-Specs
Products
MSDS
Product Shelf Life
PDS and Other Docs
Chemical.net
 
QC BLU DEF Disel Exhaust Fluid

ExxonMobile
Castrol
Shell
Valvoline
Anderol
LHB Industries
 

     Tectyl


advanced

  Tectyl 511M Class I

Military Specification MIL-PRF-16173E

TECTYL 511M, Class I

TECTYL 511M, Class I is a solvent cutback, water displacing corrosion preventive compound. The semi-firm film is oily, light amber, and translucent. TECTYL 511M, Class I is approved under Military Specifications MIL-PRF-16173E, Grade 5, for Class I.

TECTYL 511M, Class I is designed to protect ferrous and non-ferrous industrial parts and transportation components during covered shipment and inside storage.
Tectyl 511M Laboratory Data Tectyl 511M Typical Properties
Tectyl 511M Flash, PMCC*, Minimum 106F
Tectyl 511M Density, Weight/Gallon @ 77F (25C) 7.19 0.1 lbs./gallon
Tectyl 511M Specific Gravity @ 60F (15.6C) 0.84
Tectyl 511M Recommended Dry Film Thickness over Metal Profile 1.3 mils
Tectyl 511M Theoretical Coverage @ Recommended DFT 2,138 sq. ft./gallon
Tectyl 511M Non-Volatile % by Weight 46 3
Tectyl 511M Non-Volatile % by Volume 40 3
Tectyl 511M Volatile Organic Content (VOC), Maximum 4.1 lbs./gallon
Tectyl 511M Approximate Dry to Touch Time @ 77F (25C) 1 hour
Tectyl 511M Cure Time 24 hours

 

Tectyl 511M Accelerated Corrosion Tests:

5% Salt Spray (Hours)
ASTM** B-117 @ Recommended DFT
(2x4x1/8 in. Polished Steel Panels)
168
100% Relative Humidity (Hours)
ASTM D-1748 @ Recommended DFT
(2x4x1/8 in. Polished Steel Panels)
4608

Tectyl 511M Surface Preparation
The maximum performance of TECTYL 511M, Class I can be achieved only when the metal surfaces to be protected are clean, dry and free of rust, oil and mill scale. Daubert Chemical Company recommends that the metal substrate temperature be 50- 95F (10-35C) at the time of product application.

Tectyl 511MStorage
Store TECTYL511M, Class I at temperatures between 50-95F (10-35C). Mild agitation is recommended prior to use.

Tectyl 511M Application
TECTYL 511M, Class I is formulated to be used as supplied. Ensure uniform consistency prior to use. Continued stirring is generally not required. If the product thickens due to cold storage or loss of solvent during use, contact Daubert Chemical Company. DO NOT THIN TECTYL 511M, Class I. Incorrect thinning will affect film build, dry time and product performance. Daubert Chemical Company recommends that the ambient and product temperature be 50 - 95F (10 - 35C) at time of application. TECTYL 511M, Class I can be spray dip or flush applied.

Tectyl 511M Storage


Store TECTYL 511M, Class I at temperatures between 50-95F (10-35C). Mild agitation is recommended prior to use.
 
Tectyl 511M Caution
Adequate ventilation is required for cure and to ensure against formation of a combustible liquid. THE PARTIALLY CURED FILM SHOULD NOT BE EXPOSED TO IGNITION SOURCES SUCH AS FLARES, FLAMES, SPARKS, EXCESSIVE HEAT, OR TORCHES. Refer to Dauberts Material Safety Data Sheet for additional handling and first aid information.
Tectyl 511M Removal
TECTYL 511M, Class I can be removed with TECTYL HPS solvent borne thinner, vapor degreasing, hot alkaline wash, or low pressure steam. TECTYL 511M, Class I can be removed from fabrics by normal dry cleaning procedures. Avoid the use of chlorinated or highly aromatic solvents when removing from painted surfaces, as these solvents may adversely affect paint.